(For further information on spectroscopy, see:
TITLE: Copiapite GDS21 DESCRIPT
MINERAL: Copiapite (Copiapite group)
ORIGINAL_DONOR: MIT Mineral Collection, Dave Sherman
CURRENT_SAMPLE_LOCATION: USGS Denver Spectroscopy Laboratory
ULTIMATE_SAMPLE_LOCATION: USGS Denver Spectroscopy Laboratory
40 kV - 30 mA, 6.5-9.5 keV (smear mount on quartz, copiapit.out);
40 kV - 30 mA, 7.3-9.5 keV (slurry onto quartz plate, copiapt2.out)
References: JCPDS #35-583, 29-714, 20-659, 19-394, 33-1472, 42-599, 27-77
Found: two members of the copiapite group; perhaps at least one additional phase
Comment: The original pattern (copiapit.out) was barren above 30 degrees; a second pattern showed little above 38 degrees but the strip chart revealed that some reflections at low 2 theta are doublets, indicating the presence of two phases having related structures. The intensity ratio is about 5:2. There are seven mineral species in the copiapite group. I have not succeeded in completely indexing the pattern, using the JCPDS data, so I don't know which copiapite species (or solid solutions) are present. EDA analysis (on the SEM) shows a aluminum and silicon in addition Fe, S, and O. This results could indicate that one of the copiapites is Al-rich. Also that a trace of quartz is present (there are what I call insignificant peaks at the positions of the strong quartz (100) and (101) reflections - insignificant because they could just as likely be background noise. A hand-specimen with crystals suitable for single- crystal X-ray diffraction would help us sort out the copiapite species present."
J.S. Huebner, J. Pickrell, and T. Schaefer, 1994, written communication.
COMPOSITIONAL_ANALYSIS_TYPE: None # XRF, EM(WDS), ICP(Trace), WChem
Yellow color, good rhombic(?) cleavage, inclined extinction, length fast, unable to get good interference figure because of preferred cleavage orientations. Trace pink transparent mineral. G. Swayze.
SPECTRAL_PURITY: 1b2b3c4_ # 1= 0.2-3, 2= 1.5-6, 3= 6-25, 4= 20-150 microns
|LIB_SPECTRA:||splib04a r 1239||0.2-3.0µm||200||g.s.= 225 µm|
|LIB_SPECTRA:||splib05a r 2201||0.2-3.0µm||200||g.s.=|
|LIB_SPECTRA:||splib06a r 6285||g.s.=|
|LIB_SPECTRA:||splib06a r 6298||g.s.=|